Rockwell hardness meter (motorized type) TRHM-B10

Rockwell hardness meter (motorized type) TRHM-B10

Rockwell hardness meter (motorized type) TRHM-B10 with three kinds of measurement method, 7 steps of testing force meets the need of many kinds of hardness test requirements for users. Testing force in the hardness tester can be loaded, kept & unloaded automatically. The large LCD screen display the measuring data, hardness conversion values between Rockwell, brinell, Vickers scale. With unique inside structure, high measurement accuracy and reliable performance it finds application in metal & non-destructive material industry.

Preliminary test force 98 N
Total test force 588, 980, 1471 N
Brinell hardness test 306, 613, 1839 N
Vickers hardness test 294, 588, 980 N
Magnification of Microscope 37.575 x
Hardness indication Analogue display
Resolution 0.5 HR
Loading control Automatic
Maximum height of specimens 180 mm
Distance from Indenter’s center to outer wall 200 mm
Dimension of the machine 560 × 260 × 760 mm
Weight 90 kg
Power supply AC 220 V, 50 Hz
  • Large LCD screen display
  • Automatic loading control
  • Stainless steel weight selection control knob
  • Cone diamond indenter and 1.58 mm Steel ball indenter
  • Outside body with cast –iron material
  • RS232 interface
  • Connection to mini printer
  • Easy to use
Motorized type Rockwell hardness tester measures the hardness of the hard metals, carburizing steel sheets, quenching steels, hard cast irons, mild steels, chemically treated metals.

Rockwell hardness meter (motorized type) TRHM-B10
Rockwell hardness meter (motorized type) TRHM-B10

NDT Testing Instruments
Rockwell hardness meter TRHM-A11

Rockwell hardness meter TRHM-A11
  • Preliminary test force
  • 98 N
  • Total test force
  • 588, 980, 1471 N
  • Total test force dwell time
  • 1 to 30 S
Rockwell hardness meter TRHM-A10

Rockwell hardness meter TRHM-A10
  • Preliminary test force
  • 98 N
  • Total test force
  • 588, 980, 1471 N
  • Total test force dwell time
  • 0 to 30 S
Digital Brinell hardness Tester TDBH-A10

Digital Brinell hardness Tester TDBH-A10
  • Test force
  • 612.5 N, 980 N, 1225 N
  • Brinell hardness test
  • 1837.5 N, 2450 N, 4900 N/7350 N, 9800 N, 14700 N/29400 N
  • Hardness measuring area
  • 8 to 650 HBW (hard metals steel ball)
Digital low load Vickers Hardness tester TDVH-A10

Digital low load Vickers Hardness tester TDVH-A10
  • Test force
  • 9.8 N, 49 N, 98 N, 196 N, 294 N, 490 N
  • Hardness value symbol
  • HV1, HV5, HV10, HV20, HV30, HV250
  • Error range in display
  • ± 3.0 %, ± 2.0 %

Paper Testing Instruments
Paper air permeability tester TP-J10

Paper air permeability tester TP-J10
  • Measuring range
  • 0 to 1000 ml/min
  • Test area
  • 10 ± 0.02 cm2
  • Area differential pressure
  • 1 ± 0.01 kPa
Whiteness meter TP-A11

Whiteness meter TP-A11
  • Sample (size) length
  • Diameter ≥30 mm, Thickness ≤ 40 mm
  • System
  • D/0 lighting geometrical viewing conditions, diffuser diameter (d) 150mm, testing hole diameter 30mm
  • Light source
  • D65 as illuminating source
Electronic Tearing tester TP-J21

Electronic Tearing tester TP-J21
  • Capacity
  • 10 -16000 mN
  • Resolution
  • 0.1 mN
  • Tearing arm
  • 104 ± 1 mm
Water absorption tester TP-C20

Water absorption tester TP-C20
  • Measurement range
  • 0 to 200 mm
  • Specimen size
  • 15×250 mm
  • Division value
  • 1 mm

Plastic Testing Instruments
Charpy/ Izod Impact Tester TCI-A10

Charpy/ Izod Impact Tester TCI-A10
  • Impact Speed & Energy (charpy)
  • 2.9 m/s for 1J, 2J, 4J, 5J & 3.8 m/s for 7.5J, 15J, 25J
  • Impact energy (Izod)
  • 3.5 m/s for 1J, 2J, 4J, 5J, 7.5J, 15J, 25J
  • Resolution of impact energy
  • 0.001 J
Vicat softening temperature & HDT machine TVHT-A10

Vicat softening temperature & HDT machine TVHT-A10
  • Operating temperature
  • Ambient temperature to 300°C
  • Heating rate
  • 50°C/ h (5 ± 0.5°C/ 6 min) , 120°C/ h (12 ± 1°C/ 6 min)
  • Maximum temp. error with heating speed
  • ± 5°C under 50°C/ h, ± 1°C under 120°C/ h
Melt flow Indexer TMFI-A10

Melt flow Indexer TMFI-A10
  • Measuring range
  • 0.01 to 600.00 g/ 10 min (MFR), 0.01 to 600.00 cm/ 10 min (MVR), 0.001 to 9.999 g/cm (melt density)
  • Measuring rate
  • 0.001 S
  • Temperature range
  • 50 to 400°C
Primary adhesive tester TPAT-A10

Primary adhesive tester TPAT-A10
  • Inclined adjustable angle
  • 0 to 40°
  • Panel width
  • 120 mm
  • Test area width
  • 80 mm

Rubber Testing Instruments
No rotor rheometer TNRR-A10

No rotor rheometer TNRR-A10
  • Temperature tester
  • Room temperature to 200°C
  • Temperature display resolution
  • 0.1°C
  • Temperature control accuracy
  • ≤ ± 0.3°C
Mooney viscometer TMV-A10

Mooney viscometer TMV-A10
  • Control temperature range
  • Normal temperature to 200°C
  • Temperature display resolution
  • 0.01°C
  • Temperature control accuracy
  • ± 0.3°
DIN abrasion tester TDAT-A10

DIN abrasion tester TDAT-A10
  • Test arm weight
  • 2.5 N
  • Additional Loads
  • 2.5 ± 0.1 N, 5 ± 0.1 N, 10 ± 0.1 N,
  • Idler
  • 150 mm
Rubber-weiss plasticity testing machine TRWM-A10

Rubber-weiss plasticity testing machine TRWM-A10
  • Temperature range
  • RT 50° to 300°
  • Temperature accuracy
  • ± 1°
  • Measuring range
  • 0.01 to 25 mm

Other Testing Instruments
Benchtop gloss meter TBGM-A10

Benchtop gloss meter TBGM-A10
  • Test angle
  • 60°
  • Gloss aperture
  • 2 × 3 mm
  • Measurement range
  • 0 to 1000 GU

Popular Categories

Navigation

Contact Us Map